Objectives
The aim of this study was to evaluate the effect of the airborne-particle abrasion and liner application on the interfacial toughness between veneering porcelain and zirconia core by means of a fracture mechanics test.
Methods
Beam-shaped zirconia specimens were sectioned and divided into 4 groups according to different surface treatments as follows: Group C (control): no treatment; Group L: application of liner; Group A: airborne-particle abrasion with Al 2 O 3 (sandblasting); and Group AL: airborne-particle abrasion and application of liner. The zirconia surfaces before and after sandblasting were observed and analyzed by SEM and white light interferometer. Specimens of each pretreated group were veneered with 3 core/veneer thickness ratios of 2:3, 1:1, and 3:2, corresponding to 3 phase angles respectively. Fracture mechanics test was performed on each specimen, the energy release rate G and phase angle ψ were calculated to characterize interfacial toughness. The experimental data were analyzed statistically using three-way ANOVA and the Tukey's HSD test. The surfaces of fractured specimens were examined by SEM and EDX.
Results
At each phase angle, the interfaces with no treatment had higher mean G values than that of other groups. All the specimens showed mixed failure mode with residual veneer or liner on the zirconia surfaces.
Conclusions
The toughness of zirconia/veneer interface with no treatment is significantly higher than that of interfaces subjected to liner application and airborne-particle abrasion.
Clinical significance
Liner application and airborne-particle abrasion seem to reduce zirconia/veneer interfacial toughness. Therefore, the two surface treatment methods should be applied with caution.e followed by surgery in accordance to guidelines.